High Alumina Bricks
Fused AZS Zirconia Corundum Bricks
Lightweight Mullite Bricks
Andalusite Bricks
Low Creep High Alumina Bricks
Fire Clay Bricks
Acid-Resistant High Alumina Bricks
Low Creep Fire Clay Bricks
High Alumina Insulation Bricks
Phosphate High Alumina Bricks
High Alumina Refractory Bubble Bricks
Corundum Bricks
Corundum Mullite Bricks
Chrome Corundum Bricks
High Alumina Refractory Castables
Corundum Castables
Corundum Mullite Castables
Zirconia-Corundum Casting Castables
Steel Fiber Castables
Mullite Castables
High Alumina Insulating Castables
Silicon Carbide Castables
Magnesia Alumina Spinel Castables
Refractory Ramming Mass
High Alumina Refractory Mortar
High Alumina Refractory Cement
Acid Resistant Castables
Alkali Proof Castables
Magnesia Bricks
Silica Bricks
Silicon Carbide Refractories
Refractory Precast Blocks
Chrome Corundum Casting Castables
Chrome Corundum Refractory Bricks
Refractory Ceramic Balls
Refractory Honeycomb Ceramic Regenerator
Refractory Corundum Ceramic Balls
Home > News
The use temperature of refractory bricks should be distinguished according to the material of the refractory bricks. For example, refractory bricks can be divided into five categories according to the different compositions of the refractory bricks: silicon-aluminum series refractory bricks, alkaline series refractory bricks, carbon-containing refractory bricks, Zirconium-containing refractory bricks and insulating refractory bricks have different temperatures depending on the raw materials.
High-alumina refractory bricks are used in the high-temperature area of the kiln lining, and the use area is in the 1300-1400°C range. If the temperature exceeds 1400°C, anti-flaking high-alumina refractory bricks or corundum bricks must be used. The high-alumina refractory bricks used in the burner part should be mullite refractory bricks or corundum-mullite refractory bricks, with a service temperature of 1300 to 1600°C. That is, it is resistant to high temperatures, wear-resistant, corrosion-resistant, and flexible. If andalusite or cordierite is added to high alumina bricks, the service temperature of this special refractory brick is between 1350-1500°C.
Ordinary clay refractory bricks have good thermal shock and are used for general kiln linings. The operating temperature is around 1250°C. If it is a low-gas clay brick, it can be used in glass kilns and some special kiln linings. The operating temperature is above 1350°C. If andalusite or cordierite is added to clay refractory bricks, the use temperature will be above 1400°C.
The use temperature of corundum refractory bricks is higher, above 1700°C. And high strength. Refractory bricks made of corundum refractory bricks and silicon carbide are not only resistant to high temperatures, and have good strength, but also have excellent wear resistance. If it is an alkali-resistant refractory brick, the general use temperature of alkali-resistant bricks is below 1200°C. If it is a magnesia alkaline brick, the use temperature is between 1500-1650°C.
If it is a lightweight clay refractory brick series, the temperature used in the insulation area is in the range of 1000-1200°C. If it is a lightweight high-alumina refractory brick, it is used in the thermal insulation area. It plays the role of heat preservation and the operating temperature is between 1200-1350°C. It can only be used for thermal insulation and cannot be used on the working layer. Mullite polylight refractory bricks are used in the insulation layer, and the service temperature is between 1400-1500°C. If it is alumina hollow ball refractory bricks, it can be used as a heat preservation area or directly used as a working layer. The operating temperature is 1600-1700°C.